ZINC RICH PRIMER
$ 10.61
Description ZINC RICH PRIMER EPOXY KNOWN FOR OUTSTANDING CORROSION RESISTANCE FOR STEEL PARTS ONLY PC1206 ZINC RICH PRIMER CHEMISTRY Epoxy REGULAR CURE TEMP 10 Minutes@ 350°F MIN TEMP NA MAX TEMP NA RECOMMENDED THICKNESS 1.5 TO 2.5 MILS PENCIL HARDNESS 2H SPECIFIC GRAVITY 2.95 /- .05 THEORETICAL COVERAGE NA PENCIL HARDNESS 2H minimum GLOSS LEVEL (60°) 60-85 SALT SPRAY 1,000 hours BALL IMPACT 80 in/lb SDS Sheet info # #1 – Zinc Primer SDS link https://emeraldcoatings.com/sds-sheets/ ZINC RICH PRIMER EPOXY KNOWN FOR OUTSTANDING CORROSION RESISTANCE FOR STEEL PARTS ONLY,*When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.
